Thermoplastic resin composition

ABSTRACT

Thermoplastic resin compositions of improved lubricity and wear resistance are prepared without sacrificing the excellent moldability which is inherent in thermoplastic resins which compositions comprise a base resin, a lubricant and an ethylene-vinyl acetate copolymer.

RELATED APPLICATIONS

This application is a continuation-in-part of application Ser. No. 452,690 filed Mar. 19, 1974, which is, in turn, a continuation-in-part of application Ser. No. 429,083 filed Dec. 28, 1973, both now abandoned.

BACKGROUND OF THE INVENTION

In order to improve the lubricity and the wear resistance of thermoplastic resins such as nylon and polyacetal which have been used as bearing materials, etc., it has been the practice to incorporate into these resins liquid or solid lubricants such as molybdenum disulfide, graphite and polytetrafluoroethylene.

However, molybdenum disulfide, polytetrafluoroethylene and the like are expensive and do not achieve the desired results to a high degree. Moreover, their presence adversely affects the moldability of the resin. A particular problem is that when nylon, polyacetal or similar thermoplastic resin with an added lubricant is subjected to a molding process such as by extrusion molding or screw injection molding technique, the blend fails to fill the molding cavity completely and conform faithfully to its contours. Consequently, the desired molded products are not obtained. To avoid the difficulty, compression molding or the method whereby a sintered resin is immersed in a liquid lubricant are normally employed. With these methods, however, it is difficult to efficiently produce large numbers of molded products of complicated shapes.

Recently a method has been disclosed which enables an oil to be incorporated in nylon or polyacetal (Japanese Official Gazette of Patent Publication No. 5321/1971). This method requires the resin to be treated at an elevated temperature for an extended period of time in the lubricant oil. Unfortunately, this gives rise to the possiblity of degradation of the resin. In addition, this method requires special mechanical equipment which increases the cost and decreases the productivity. Moreover, pellets produced by this method, when subjected to extrusion molding or screw injection molding, tend to bleed out the lubricant which seriously impairs the efficiency of the molding machine. This method, despite elaborate precautions produces molded products in which the surface is wet with lubricant.

It has now been discovered that the addition of a third component, namely an ethylene-vinyl acetate copolymer substantially alleviates the problems aforesaid, and permits the production of molded products of complicated design which have excellent lubricity without a wet surface, and excel in wear resistance. Moreover, the products can be produced at high production rates.

SUMMARY OF THE INVENTION

The compositions of this invention are novel resin compositions excelling in moldability, lubricity and wear resistance, which composition comprise from 55 to 99.5 percent by weight of thermoplastic resin, from 0.3 to 25 percent by weight of a lubricant and from 0.2 to 20 percent by weight of an ethylene-vinyl acetate copolymer in such amounts to make up 100 percent by weight.

DETAILED DESCRIPTION OF THE INVENTION

Any of a wide variety of thermoplastic resins may be employed as the principal component of the compositions of this invention. These include, for example, polyacetal, nylon, polyethylene, polypropylene, polyphenylene sulfide and polysulfone. The invention is particularly useful with polyacetals or nylons which are used in bearings and gears and have excellent solvent resistance. Typically useful polyacetals include homopolymers or copolymers containing 1 to 10 mol % of a cyclic ether. Typically useful nylons include nylon 6, nylon 6.6, nylon 6.10 or nylon 6.12.

When the compositions contain appreciably more than 99.5 percent by weight resin the desired effect of the lubricant upon lubricity and wear resistance is not achieved. When less than 55 percent by weight is employed the products are not sufficiently rigid. The preferred compositions contain from 70 to 98 percent by weight, respectively based on the weight of the composition.

Substantially any liquid lubricant which does not dissolve the resin can be used. These include, for example, paraffins of the type which are solid at normal room temperature and which become liquid during the production of the composition of this invention. Typical examples of desirable liquid lubricants include paraffin, naphthene, and aromatic type oils, polyalkylene glycol type oils, ester type oils, e.g. mono- and polyalcohol esters of organic and inorganic acids such as monobasic fatty acids, dibasic fatty acids, phthalic acid and phosphoric acid. Blends of these oils may also be employed.

The amount of the lubricant is generally from 0.3 to 25 percent, preferably between 1 to 15 percent, by weight based on the weight of the composition. When the amount of the lubricant is appreciably less than 0.3 percent by weight, the lubricant's effort upon lubricity and wear resistance is substantially lost. If the amount substantially exceeds 25 percent by weight, however, the stiffness of the finished composition is seriously affected.

The ethylene-vinyl acetate copolymer absorbs the lubricant and swells, but does not dissolve in the lubricant at normal room temperature. Ethylene-vinyl acetate copolymers used in this invention normally contain from 15 to 50 percent, preferably 19 to 28 percent, by weight of vinyl acetate comonomer. Melt index (MI) of the copolymer is typically from 0.1 to 300 g/10 min. as measured by ASTM D1238.

The amount of ethylene-vinyl acetate copolymer employed in the compositions of the invention is normally from 0.2 to 20 percent, preferably from 1 to 15 percent, by weight. When the amount of ethylene-vinyl acetate copolymer is noticeably less than 0.2 percent by weight, the ability of the composition to provide good transporting property of the screw during the molding operation is decreased. When the amount appreciably exceeds 20 percent by weight, however, the stiffness of the composition is seriously lowered.

In addition to the base resin, the lubricant and the ethylene-vinyl acetate copolymer described hereinabove, the compositions of this invention can include the usual reinforcing agents, extenders, additives, etc., which are generally employed with such resins. These may also include solid lubricants such as graphite, molybdenum disulfide, fluorocarbon resins and metallic soaps; inorganic filters; glass fiber; pigments; flame retardants; antistatic agents and various stabilizers.

The combination of the aforementioned three essential components, that is, base resin, lubricant and ethylene-vinyl acetate copolymer, must be selected properly bearing in mind their respective properties. When resins such as polyphenylene sulfides or polysulfones which have relatively high molding temperatures are employed as the base resin, the lubricant selected should be capable of withstanding high molding temperatures.

The mixer utilized for producing the compositions of this invention may be any of those readily available mixers which have the necessary heat production and mixing capabilities. For example, high-speed fluid mixing devices such as the Henschel mixer, ribbon blenders and the like are advantageously used. Devices which are not adapted to permit heating may be used if the individual components of the resin composition are heated in advance.

In one typical method employed for producing the compositions of this invention, the base resin in the form of powder or pellets, the lubricant and the ethylene-vinyl acetate copolymer in the form of powder or pellets are agitated and mixed at a temperature below the melting point of the base resin or, in the case of a noncrystalline resin, at a temperature below the point at which the resin melts and coagulates, until the lubricant has thoroughly been absorbed by the ethylene-vinyl acetate copolymer. This usually requires about ten minutes, although it may vary appreciably depending on the quantities of the components, the rate of mixing, the particular resin and lubricant selected and the temperature. The composition thus produced may be pelletized in an extruding device and the pellets thereafter molded. In this case, the amount of the lubricant employed is from 0.2 to 8 times that of the ethylene-vinyl acetate copolymer, so as to obtain the desired results with respect to friction property and wear resistance and transporting property of the screw of the extruding device.

Alternatively, the compositons may be prepared by initially mixing the base resin and the ethylene-vinyl acetate copolymer, and subsequently introducing the lubricant dropwise into the resultant mixture while under agitation so that it may be absorbed into the mixture.

The compositions may also be produced by first introducing the lubricant dropwise into the ethylene-vinyl acetate copolymer while under agitation and, after the lubricant has thoroughly been absorbed, adding the base resin to the resultant mixture. Thus, the sequence of mixing, the method of addition of the lubricant, the method of heating the mixture, etc., may advantageously be selected from a variety of possibilities.

For optimum convenience, the base resin and the ethylene-vinyl acetate copolymer selected for the production of the compositions of this invention are normally in the form of finely divided particles capable of passing a sieve of a mesh size 10. This is not essential, however, They may be used in the form of pellets.

The pellets formed by any of the methods described above may be utilized directly for extrusion or injection molding. It is not necessary to form the compositions into pellets, however, since they can be formed and utilized in any of a variety of geometrical configurations.

Compared with the lubricant-containing resin obtained by the sintering method or the method disclosed by the Japanese Official Gazette of Patent Publication No. 5321/1971 which has heretofore been used, the pelletized composition of the present invention suffers far less from the phenomenon of heat degradation due to prolonged heating. Moreover, since no special equipment is required, molded products can be produced in large quantities in a short period of time.

The pelletized compositions of this invention can be utilized for injection, extrusion, or blow molding and similar procedures, with the transporting property of the screw improved to a great extent. The compositions in a pulverized form can be used in rotational molding.

In addition to improved moldability, other factors which contribute to the value of the novel compositions of this invention are improved lubricity and wear resistance. Conventional compositions include only the resin and the lubricant. The products of this invention, however, additionally contain an ethylene-vinyl acetate copolymer system. The copolymer retains the lubricant in an abosorbed state so that bleed out of the lubricant on the resin surface is minimized. The lubricity and wear resistance offered by this composition immediately after molding is equivalent to that of the conventional systems. However, even after a prolonged service, the surface of the molded product is wetted only slightly as a result of bleeding out of the lubricant. Thus, the surface does not become sticky and the abrasion resistance is not degraded.

The mold shrinkage and impact resistance of the compositions obtained in accordance with the present invention are also excellent.

the following non-limiting examples are given by way of illustration only.

Examples 1 and 2 and Comparative Examples 1-1, 1-2, 1-3, 2-1, 2-2 and 2-3:

Polyacetal homopolymer (MI 7.0 g/10 min. 190° C.) or nylon 6 (relative viscosity is sulfuric acid 2.5) in the powdered form was used as the thermoplastic resin, a paraffin type oil (SUS 460 100° F.) or naphthene type oil (SUS 370 100° F.) was used as the lubricant, and ethylene-vinyl acetate copolymers (EVA MI 150 g/10 min. and having a vinyl acetate content of 19 percent by weight; MI 15 g/10 min. and having a vinyl acetate content of 28 percent by weight) in the powdered form were used as the ethylene-vinyl acetate copolymer, respectively in amounts to give percent compositions shown in Table 1. Each charge was mixed while heating in a Henschel mixer at temperatures below the point at which the resins would be melted and converted into a viscous solidified mass. The resultant mixture composition was pelletized by means of an extruder.

In Comparative Examples 1-2, 2-2 and 2-3, the preparation of pellets was carried out in accordance with the method disclosed in the Japanese Official Gazette of Patent Publication No. 5321/1971.

These pellets and pellets of polymers used as base resins were subjected to injection molding. The results are shown in Table 1. As is clear from this table, the pellet compositions according to this invention could be injection molded in the same way as the pellets of base resins to afford test pieces with good lubricity, wear resistant and high dimensional accuracy, whereas the pellet compositions of the resin + lubricant system could not be injection molded because of inferior transporting property of the screw. Consequently, wear resistant test pieces with good lubricity were obtained from these compositions by using the compression molding technique.

The results of the lubricity and wear resistance test performed on such test pieces are shown in Table 1. As is clear from this table, the compositions according to this invention are superior to the conventional lubricant-containing resin compositions in molding property, particularly in terms of transporting property of the screw and decreased bleed out. As concerns the properties of lubricity and wear resistance, they showed a lower friction coefficient than the base resins. The state of wear was satisfactory and equivalent to that of the conventional lubricant-containing resin composition. Thus, the improved properties of the resin compositions of this invention were evident.

Examples 3-1, 3-2, 3-3, 3-4, 3-5, 3-6, 3-7, 3-8, 3-9, 3-10, 3-11, and Comparative Examples 3-1, 3-2, 3-3, 3-4, 3-5, 3-6, 3-7 and 3-8:

The compositions of the formulations shown in Example 1 and Example 2 were combined with the other formulations shown in Table 2-1 and Table 2-2, subjected to test molding, and thereafter tested for physical properties.

For comparison, compositions having the proportions of components varied so as to be outside of the stated range of formulation were subjected to the same test. The results are included in said table.

As is apparent from Table 2-1 and Table 2-2, molded products of compositions using resins in amounts smaller than the lower limit of said range exhibited lower stiffness and those of compositions using lubricants in amounts smaller than the lower limit failed to produce the effect of lubricant upon lubricity and wear resistance. It is also apparent that the transporting property of the screw was adversely affected when the ratio of lubricant and ethylene-vinyl acetate copolymer were increased beyond their respective upper limits and that the lubricant's effect upon lubricity and wear resistance was lost when their ratio were decreased below their respective lower limits.

Examples 4, 5 and 6 and Comparative Examples 4-1, 4-2, 4-3, 5-1, 5-2, 5-3, 6-1, 6-2 and 6-3.

The procedures of Examples 1 and Comparative Examples 1-1, 1-2 and 1-3 were repeated, except polyacetal homopolymers containing glass fiber, molybdenum disulfide (MoS₂) and graphite respectively were used in place of base polymers. The resultant compositions were tested for moldability and physical properties.

The results are shown in Table 3. From the table, the effects of the Compositions (Example 4, 5 and 6) according to the present invention were evident as in the case of Example 1.

Examples 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17 and 18:

The procedures of Example 1 and Example 2 were repeated, except aromatic type oil (having aromatic content of 50% by weight, 15 cst, 100° F.), polyalkylene glycol oil (35 cst, 100° F.), butyl stearate, dioctyl sebacate, dioctyl phthalate and tricresyl phosphate were used in place of the lubricants of Example 1 and Example 2. The resultant compositions were tested for moldability and physical properties.

The results are shown in Table 4. From the table, the effects of the compositions were evident as in the case of Example 1 and Example 2.

Examples 19, 20, 21, 22 and 23:

The procedures of Example 2 were repeated, except acetal copolymer (copolymer of trioxan and cyclic ether, MI 13.0 g/10 min. 190° C.), nylon 6.6 (relative viscosity in sulfuric acid 2.5), nylon 6.10 (relative viscosity in sulluric acid 2.6) nylon 6 containing glass fiber and nylon 6.6 containing graphite were used in place of nylon 6. The resultant compositions were tested for moldability and physical properties.

The results are shown in Table 5. From the table, the effects of the compositions were evident as in the case of Example 1.

                                      Table 1                                      __________________________________________________________________________     Test for moldability and physical properties (1)                                                                     Friction property and                                                          wear resistance test                                                           (test condition-resin-                                                         to-resin under load of                                                         2 kg/cm.sup.2)                                  Formulation                    Friction     Surface                     Test for                                                                              (percent by weight)                                                                            Moldability    coefficient  wetting of                  moldability      Ethylene-   Cylinder (μ)       molded                      & physical       vinyl       temper-                                                                             Cycle                                                                              (linear      product with                properties                                                                            Base      acetate                                                                              Molding                                                                              ature                                                                               time                                                                               speed 1                                                                               Condition                                                                            bleeded out                 (1)    resin                                                                              Lubricant                                                                            copolymer                                                                            process                                                                              (° C)                                                                        (sec)                                                                              cm/sec)                                                                               of wear                                                                              oil                         __________________________________________________________________________     Example 1                                                                             Poly-                                                                              Paraffin                                                                             EVA   Injection                                                                            200  (45)                                                                               0.10 - 0.15                                                                           Absolutely                                                                           Practically                        acetal                                                                             type oil                                                                             (vinyl                                                                               molding               no wear                                                                              no wetting                         (90)                                                                               (5)   acetate                     observed.                                          content                                                                        19% by                                                                         weight)                                                                        (5)                                                           Comparative                                                                           Poly-                                                                               --    --   Injection                                                                            200  (45)                                                                               0.30 - 0.35                                                                           Worn  None                        Example 1-1                                                                           acetal          molding               powder                                   (100)                                 appeared                                                                       over about                                                                     10 cm/sec                         Comparative                                                                           Poly-                                                                              Paraffin                                                                              --   Injection                                                                            200  (∞)                                                                          --      --    --                         Example 1-2                                                                           acetal                                                                             type oil    molding    Poor                                                (95)                                                                               (5)                    trans-                                                                         porta-                                                                         tion                                         Comparative                                                                           Poly-                                                                              Paraffin                                                                              --   Compres-                                                                             --   --  0.10 - 0.15                                                                           Absolutely                                                                           Unusually                   Example 1-3                                                                           acetal                                                                             type oil    sion                  no wear                                                                              heavy                              (95)                                                                               (5)         molding               observed.                                                                            wetting                                                                        observed                    Example 2                                                                             Nylon                                                                              Naphthene                                                                            EVA   Injection                                                                            210  (60)                                                                               0.05 - 0.10                                                                           Absolutely                                                                           Practically                        (90)                                                                               type oil                                                                             (vinyl                                                                               molding               no wear                                                                              no wetting                             (5)   acetate                     observed.                                          content                                                                        28% by                                                                         weight)                                                                        (5)                                                           Comparative                                                                           Nylon                                                                               --    --   Injection                                                                            210  (60)                                                                               0.40 - Worn5 None                        Example 2-1                                                                           (100)           molding               powder                                                                         appeared                                                                       over                                                                           about 10                                                                       cm/sec.                           Comparative                                                                           Nylon                                                                              Naphthene                                                                             --   Injection                                                                            210  (∞)                                                                          --      --    --                         Example 2-2                                                                           (95)                                                                               type oil    molding    Poor                                                    (5)                    trans-                                                                         porta-                                                                         tion                                         Comparative                                                                           Nylon                                                                              Naphthene                                                                             --   Compres-                                                                             --   --  0.05 - 0.10                                                                           Absolutely                                                                           Unusually                   Example 2-3                                                                           (95)                                                                               type oil    sion                  no wear                                                                              heavy                                  (5)         molding               observed.                                                                            wetting                                                                        observed.                   __________________________________________________________________________

                                      Table 2-1                                    __________________________________________________________________________     Test for moldability and physical properties (2-1)                                                                        Friction property and                                                          wear resistance test                                                           (test condition-resin                      Formulation                                                                    to-resin, under load                                                           (percent by weight)                 of 2 kg/cm.sup.2)                                  EVA                Moldability                                                                             Friction     Surface                Test for       (vinyl             (by injection                                                                           coefficient  wetting of             moldability                                                                               Paraf-                                                                             acetate    Degree of                                                                              molding) (μ)       molded                 & physical fin content:   pelletiza-                                                                             Cylinder                                                                            Cycle                                                                              (linear      product with           properties                                                                            Poly-                                                                              type                                                                               19% by                                                                              Oil (wt%)                                                                            tion of tempera-                                                                            time                                                                               speed  Condition                                                                            bleeded out            (2-1)  acetal                                                                             oil weight)                                                                             EVA (wt%)                                                                            composition                                                                            ture (sec)                                                                              1 cm/sec.)                                                                            of wear                                                                              oil                    __________________________________________________________________________     Example 3-1                                                                           90  5   5    1     Good    200  45  0.10 - 0.15                                                                           Absolutely                                                                           Practically                                                              no wear                                                                              no wetting                                                               observed.                    Comparative                                                                           99.9                                                                               0.05                                                                               0.05 1     Good    200  45  0.30 - 0.35                                                                           Worn  None                   Example 3-1                                       powder                                                                         appeared                                                                       over 10                                                                        cm/sec.                      Example 3-2                                                                           99  0.5 0.5  1     Good    200  45  0.20 - 0.25                                                                           Absolutely                                                                           None                                                                     no wear                                                                        observed.                    Example 3-3                                                                           70  15  15   1     Good    200  45  0.10 - 0.15                                                                           Absolutely                                                                           Practically                                                              no wear                                                                              no wetting                                                               observed.                    Comparative                                                                           40  30  30   1     Pelletization                                                                          200  50  0.15 - 0.20                                                                           Sample                                                                               Wetting                Example 3-2               was                     was                                                    difficult               deformed                                               because of              because of                                             low stiffness           low                                                                            stiffness.                   Comparative                                                                           90  9.9 0.1  99    No trans-                                                                              --   --  --     --    --                     Example 3-3               portation                                                                      was                                                                            obtained                                                                       with                                                                           extruder.                                            Example 3-4                                                                           90  6.7 3.3  2     Good    200  45  0.10 - .015                                                                           Absolutely                                                                           Practically                                                              no wear                                                                              no wetting                                                               observed.                    Example 3-5                                                                           90  3.3 6.7  0.5   Good    200  45  0.10 - 0.15                                                                           Absolutely                                                                           Practically                                                              no wear                                                                              no wetting                                                               observed.                    Comparative                                                                           90  0.1 9.9  0.01  Good    200  45  0.30 - 0.35                                                                           Worn  None                   Example 3-4                                       powder                                                                         appeared                                                                       over                                                                           15 cm/sec.                   __________________________________________________________________________

                                      Table (2-2)                                  __________________________________________________________________________     Test for moldability and physical properties (2-2)                                                                       Lubricity &                                                                    wear resist-                                                                   ance test                                                                      (test condi-                                                                   tion-resin-                                                                    to-resin under                                                                 load of 2 kg/                                                                  cm.sup.2)                                   Formulation                        Fric-                                       (percent by weight)       Moldability                                                                             tion                                                 EVA              (by injec-                                                                              coef-                                Test for        (vinyl           tion molding)                                                                           ficient      Surface                 moldability                                                                               Paraf-                                                                              acetate                                                                             Oil Degree of                                                                              Cylind-  (μ)       wetting of              & physical fin  content                                                                             (wt %)                                                                             Pelletiz-                                                                              er temp-                                                                            Cycle                                                                              (linear      molded prod-            properties                                                                            Nylon                                                                              type 19% by                                                                              EVA ation of                                                                               erature                                                                             time                                                                               speed                                                                               Condition                                                                              uct from                (2-2)                                                                          6      oil weight)                                                                             (wt %)                                                                              composition                                                                        (° C)                                                                           sec  1 cm/sec)                                                                          of wear                                                                             bleed out                       __________________________________________________________________________                                                    oil                             Example                                                                               90  5    5    1   Good    230  60  0.05-                                                                               Absolute-                                                                              Practically             3-6                                       0.10 ly no wear                                                                             no wetting                                                             observed.                       Compara-                                                                              99.9                                                                               0.05 0.05 1   Good    230  60  0.35-                                                                               Worn powd-                                                                             None                    tive Ex-                                  0.40 er appear-                      ample 3-5                                      ed over                                                                        10cm/sec.                       Example                                                                               99  0.5  0.5  1   Good    230  60  0.20-                                                                               Absolute-                                                                              None                    3-7                                       0.25 ly no wear                                                                     observed.                       Example                                                                               70  15   15   1   Good    230  60  0.05-                                                                               Absolute-                                                                              Practically             3-8                                       0.10 ly no wear                                                                             no wetting                                                             observed.                       Compara-                                                                              40  30   30   1   Pelletiz-                                                                              230  80  0.05-                                                                               Sample was                                                                             Wetting                 tive Ex-                 ation was        0.10 deformed                        ample 3-6                difficult             because of                                               because of            low stiffness.                                           low stiffness                                         Compara-                                                                              90  9.9  0.1  99  No trans-                                                                              --   --   --   --      --                     tive Ex-                 portation                                             ample 3-7                was ob-                                                                        tained with                                                                    extruder                                              Example                                                                               90  6.7  3.3  2   Good    230  60  0.05-                                                                               Absolute-                                                                              Practically             3-9                                       0.10 ly no wear                                                                             no wetting                                                             observed.                       Example                                                                               88  9    3    3   Good    230  60  0.05-                                                                               Absolute-                                                                              Practically             3-10                                      0.10 ly no wear                                                                             no wetting                                                             observed.                       Example                                                                               90  3.3  0.7  0.5 Good    230  60  0.10-                                                                               Absolute-                                                                              None                    3-11                                      0.15 ly no wear                                                                     observed.                       Compara-                                                                              90  0.1  9.9  0.01                                                                               Good    230  60  0.30-                                                                               Worn powder                                                                            None                    tive Ex-                                  0.35 appeared over                   ample 3-8                                      10cm/sec.                       __________________________________________________________________________

                                      Table 3                                      __________________________________________________________________________     Test for moldability and physical properties (3)                                                                           Friction property                                                              and wear resistance                                                            test (test condition                                                           resin-to-resin                                                                 under load of                                                                  2 kg/cm.sup.2)                                                                 Friction                                                                       coef-       Surface                Test for                                                                              Formulation (percent by weight)                                                                      Moldability    ficient     wetting of             moldability       Ethylene         Cylinder (μ)      molded                 & physical                                                                     vinyl             tempera-                                                                             Cycle                                                                               (linear    product with                           properties                                                                            Base       acetate    Molding                                                                              ture time                                                                               speed 1                                                                              Condition                                                                            bleeded out            (3)    resin                                                                               Lubricant                                                                            copolymer                                                                            Additive                                                                            process                                                                              (° C)                                                                        (sec)                                                                              cm/sec)                                                                              of wear                                                                              oil                    __________________________________________________________________________     Example 4                                                                             Poly-                                                                               Paraf-                                                                               EVA   Glass                                                                               Injection                                                                            200  (50)                                                                               0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              fin   (VA   fiber                                                                               molding              no wear                                                                              no wetting                    (80) type oil                                                                             content                                                                              (10)                      observed.                                (5)   19% by                                                                         weight)                                                                        (5)                                                          Comparative                                                                           Poly-                                                                               Paraffin                                                                              --   Glass                                                                               Injection                                                                            200  (∞)                                                                          --     --   --                     Example 4-1                                                                           acetal                                                                              type oil    fiber                                                                               molding    No                                            (85) (5)         (10)            trans-                                                                         porta-                                                                         tion                                   Comparative                                                                           Poly-                                                                               Paraffin                                                                              --   Glass                                                                               Compres-                                                                             --    -- 0.10-0.15                                                                            Absolutely                                                                           Unusually              Example 4-2                                                                           acetal                                                                              type oil    fiber                                                                               sion                 no wear                                                                              heavy                         (85) (5)         (10) molding              observed.                                                                            wetting                                                                        observed.              Comparative                                                                           Poly-                                                                                --    --   Glass                                                                               Injection                                                                            200  (50)                                                                               0.35-0.40                                                                            Worn  None                   Example 4-3                                                                           acetal           fiber                                                                               molding              powder                              (90)             (10)                      appeared                                                                       over 5                                                                         cm/sec                       Example 5                                                                             Poly-                                                                               Paraffin                                                                             EVA (VA                                                                              MoS.sub.2                                                                           Injection                                                                            200  (45)                                                                               0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              type oil                                                                             content                                                                              (2)  molding              no wear                                                                              no wetting                    (88) (5)   19% by                          observed.                                      weight                                                                         (5)                                                          Comparative                                                                           Poly-                                                                               Paraffin                                                                              --   MoS.sub.2                                                                           Injection                                                                            200  (∞)                                                                          --    --    --                     Example 5-1                                                                           acetal                                                                              type oil    (2)  molding    No                                            (93) (5)                         trans-                                                                         porta-                                                                         tion                                   Comparative                                                                           Poly-                                                                               Paraffin                                                                              --   MoS.sub.2                                                                           Compres-                                                                             --    -- 0.10-0.15                                                                            Absolutely                                                                           Unusually              Example 5-2                                                                           acetal                                                                              type oil    (2)  sion                 no wear                                                                              heavy                         (93) (5)              molding              observed.                                                                            wetting                                                                        observed.              Comparative                                                                           Poly-                                                                                --    --   MoS.sub.2                                                                           Injection                                                                            200  (45)                                                                               0.30-0.35                                                                            Worn  None                   Example 5-3                                                                           acetal           (2)  molding              powder                              (98)                                       appeared                                                                       over 10                                                                        cm/sec.                      Example 6                                                                             Poly-                                                                               Paraffin                                                                             EVA (VA                                                                              Graphite                                                                            Injection                                                                            200  (45)                                                                               0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              type oil                                                                             content                                                                              (5)  molding              no wear                                                                              no wetting                    (85) (5)   19% by                          observed.                                      weight)                                                                        (5)                                                          Example 6-1                                                                           Poly-                                                                               Paraffin                                                                              --   Graphite                                                                            Injection                                                                            200  (∞)                                                                          --    --    --                            acetal                                                                              type oil    (5)  molding    No                                            (85) (5)                         trans-                                                                         porta-                                                                         tion                                   Example 6-2                                                                           Poly-                                                                               Paraffin                                                                              --   Graphite                                                                            Compres-                                                                             --    -- 0.10-0.15                                                                            Absolutely                                                                           Unusually                     acetal                                                                              type oil    (5)  sion                 no wear                                                                              heavy                         (85) (5)              molding              observed.                                                                            wetting                                                                        observed.              Example 6-3                                                                           Poly-                                                                                --    --   Graphite                                                                            Injection                                                                            200  (45)                                                                               0.30-0.35                                                                            Worn  None                          acetal           (5)  molding              powder                              (85)                                       appeared                                                                       over 20                                                                        cm/sec.                      __________________________________________________________________________

                                      Table 4                                      __________________________________________________________________________     Test for moldability and physical properties (4)                                                                           Friction property and                                                          wear resistance test                                                           (test condition-resin                     to-resin, under load                                                           Formulation                          of 2 kg/cm.sup.2)                         (percent by weight)                  Friction                                             EVA              Moldability                                                                             coef-       Surface                Test for          (vinyl     Degree of                                                                            (by injection                                                                           ficient     wetting of             moldability       acetate    pelletiza-                                                                           molding) (μ)      molded                 & physical        content:   tion of                                                                              Cylinder                                                                            Cycle                                                                              (linear     product with           properties                                                                            Base Lubri-                                                                               19% by                                                                              Oil (wt %)                                                                           compo-                                                                               temper-                                                                             time                                                                               speed Condition                                                                            bleeded out            (4)    resin                                                                               cant  weight)                                                                             EVA (wt %)                                                                           sition                                                                               ature                                                                               (sec)                                                                              1 cm/sec.)                                                                           of wear                                                                              oil                    __________________________________________________________________________     Example 7                                                                             Poly-                                                                               Aromatic                                                                             5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              type oil                              no wear                                                                              no wetting                    90   5                                     observed.                    Example 8                                                                             Poly-                                                                               Poly- 5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              alkylene                              no wear                                                                              no wetting                    90   glycol                                observed.                                oil                                                                            5                                                                  Example 9                                                                             Poly-                                                                               Butyl 5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              stearate                              no wear                                                                              no wetting                    90   5                                     observed.                    Example 10                                                                            Poly-                                                                               Dioctyl                                                                              5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              sebacate                              no wear                                                                              no wetting                    90   5                                     observed.                    Example 11                                                                            Poly-                                                                               Dioctyl                                                                              5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              phthalate                             no wear                                                                              no wetting                    90   5                                     observed.                    Example 12                                                                            Poly-                                                                               Tricresyl                                                                            5    1     Good  200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   acetal                                                                              phosphate                             no wear                                                                              no wetting                    90   5                                     observed.                    Example 13                                                                            Nylon                                                                               Aromatic                                                                             5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   type oil                              no wear                                                                              no wetting                         5                                     observed.                    Example 14                                                                            Nylon                                                                               Poly- 5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   alkylene                              no wear                                                                              no wetting                         glycoloil                             observed.                    Example 15                                                                            Nylon                                                                               Butyl 5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   stearate                              no wear                                                                              no wetting                         5                                     observed.                    Example 16                                                                            Nylon                                                                               Dioctyl                                                                              5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   Sebacate                              no wear                                                                              no wetting                         5                                     observed.                    Example 17                                                                            Nylon                                                                               Dioctyl                                                                              5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   phthalate                             no wear                                                                              no wetting                         5                                     observed.                    Example 18                                                                            Nylon                                                                               Tricresyl                                                                            5    1     Good  230  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90   phosphate                             no wear                                                                              no wetting                         5                                     observed.                    __________________________________________________________________________

                                      Table 5                                      __________________________________________________________________________     Test for moldability and physical properties (5)                                                                           Lubricity &                                                                    wear resist-                                                                   ance test                                                                      (test condi-                                                                   tion-resin-                                                                    to-resin under                                                                 load of 2kg/                                                                   cm.sup.2)                                 Formulation                          Fric-                                     (percent by weight)         Moldability                                                                             tion                                                  EVA             (by injec-                                                                              coef-                              Test for           (vinyl          tion molding)                                                                           ficient     Surface                moldability        acetate                                                                             Oil Degree Cylind-  (μ)      wetting of             & physical         content:                                                                            (wt %)                                                                             of pelleti-                                                                           er temp-                                                                            Cycle                                                                              (linear     molded pro-            properties                                                                            Base  Naphthene                                                                            28% by                                                                              EVA zation of                                                                             erature                                                                             time                                                                               speed Condition                                                                            duct from              (5)    resin type oil                                                                             weight)                                                                             (wt %)                                                                             composition                                                                           (° C)                                                                        (sec)                                                                              1cm/sec)                                                                             of wear                                                                              bleed out              __________________________________________________________________________                                                             oil                    Example 19                                                                            Acetal                                                                               5     5    1   Good   200  45  0.10-0.15                                                                            Absolutely                                                                           Practically                   Copolymer                                  no wear                                                                              no wetting                    90                                         observed.                    Example 20                                                                            Nylon 6.6                                                                            5     5    1   Good   280  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   90                                         no wear                                                                              no wetting                                                               observed.                    Example 21                                                                            Nylon 6.10                                                                           5     5    1   Good   240  60  0.10-0.15                                                                            Absolutely                                                                           Practically                   90                                         no wear                                                                              no wetting                                                               observed.                    Example 22                                                                            Nylon 6                                                                              5     5    1   Good   230  60  0.10-0.15                                                                            Absolutely                                                                           Practically                   contain-                                   no wear                                                                              no wetting                    ing 20 wt                                  observed.                           % glass                                                                        fiber 90                                                                Example 23                                                                            Nylon 66                                                                             5     5    1   Good   280  60  0.05-0.10                                                                            Absolutely                                                                           Practically                   containing                                 no wear                                                                              no wetting                    10 wt % gra-                               observed.                           phite 90                                                                __________________________________________________________________________

The foregoing examples illustrate the remarkable results which are achieved with a variety of polyacetals and nylons in accordance with the practice of this invention. Similar results are achieved in other specific examples with additional thermoplastic resins including polyethylene, polypropylene, polyphenylene sulfide and polysulfone. 

What is claimed is:
 1. A thermoplastic resin composition having excellent lubricity and wear resistance comprising from 55 to 99.5 percent by weight of thermoplastic polyacetal, from 0.3 to 25 percent by weight of a liquid lubricant which does not dissolve the resin, and from 0.2 to 20 percent by weight of an ethylene-vinyl acetate copolymer which contains from 15 to 50 percent by weight of vinyl acetate comonomer.
 2. A composition as in claim 1 wherein the lubricant is selected from the group consisting of paraffin type oils, naphthene type oils, aromatic type oils, polyalkylene glycol type oils and ester type oils.
 3. A composition as in claim 1 wherein the ethylene-vinyl acetate copolymer contains from 19 to 28 percent by weight of vinyl acetate comonomer.
 4. A composition as in claim 1, wherein the polyacetal resin is selected from the group consisting of acetal homopolymer and acetal copolymer containing 1 - 10 mol % of cyclic ether.
 5. A composition as in claim 1, wherein the thermoplastic resin content is from 70 to 98 percent by weight, the lubricant content is from 1 to 15 percent by weight, and the ethylene-vinyl acetate copolymer content is from 1 to 15 percent by weight. 